Alloy 800, UNS N08800

Incoloy 800

 

Alloy 800 (UNS N08800)

Summary

A nickel-chromium alloy with good strength and excellent resistance to oxidation and carburization in high-temperature atmospheres. It also resists corrosion by many aqueous environments. The alloy maintains a stable, austenitic structure during prolonged exposure to high temperatures. Used for process piping, heat exchangers, carburizing equipment, heatingelement sheathing, and nuclear steam-generator tubing.

Standard Product Forms

Pipe, tube, sheet, strip, plate, round bar, flat bar, forging stock, hexagon and wire.

Chemical Composition Wt,%

 

Min

Max.

 

Min.

Max.

 

Min.

Max.

Ni

30.0

35.0

Cu

 

0.75

C

 

0.1

Cr

19.0

23.0

Co

 

 

Si

 

1.0

Fe

39.5

 

Al

0.15

0.6

P

 

 

Mo

 

 

Ti

0.15

0.6

S

 

0.015

Nb

 

 

Mn

 

1.5

N

 

 

Physical

Constants

Density,g/ 7.94

Melting Range,℃ 1357-1385

Typical Mechanical Properties

(Annealed)

(1000h) Rupture Strength (1000h) ksi Mpa

1000℉/540℃ 48 360

1100℉/595℃ 32 160

1200℉/650℃ 21 50

1300℉/705℃ 11 18

 


Microstructure

Alloy 800 is an austenitic, solid-solution alloy and has a face-cetered-cubic structure. Titanium nitrides, titanium carbides, and chromium carbides normally appear in the alloy's microstructure.


Characters

Alloy 800H is characterized by:

Good creep-rupture properties at temperatures above 600℃(1110℃) without loss of ductility during long-term use at temperatures below 700℃(1290℉), due to limitation of (Ti+Al) content to max. 0.7%;

Good resistance to reducing, oxidizing and nitriding atmospheres and to atmospheres which alternate between reducing and oxidizing condition;

Metallurgical stability in long-term application at high temperatures.

Alloy 800HT is characterized by:

Excellent creep strength at temperature above 700℃. However, for application where frequent excursions lower than 700℃ during service cannot be excluded or parts of the material are permanently exposed to a temperature below 700℃, the use of Alloy 800H is recommended.

Good resistance to reducing, oxidizing and nitriding atmospheres and to atmospheres which alternate between reducing and oxidizing condition;

Metallurgical stability in long-term application at high temperatures.


Corrosion Resistance

Alloy 800, like many austenitic stainless steels, can be sensitized, or made susceptible to intergranular attack in some aggressive media, by exposure to the temperature range of 1000 to 1400℉(540-760℃).


Application

For services below 600℃ the use of soft annealed Incoloy 800 is suggested. Alloy 800 has aoolication in furnace components and equipment, petrochemical furnace cracker tubes, pigtails and headers, and sheathing for electrical heating elements.


We have products:

seamless pipe,seamless tube,

 

 

 

 

 

welded pipe,welded tube,

pipe fitting,flange,bar,plate


Complete inspection equipment and quality system.
Eddy current test, Ultrasonic detector, hydraulic test equipment, Universal testing machine, Arldirect-reading spectrometer...... Recently we have replaced a new set of advanced PMI equipment, OXFORD INSTRUMENTS X-MET7000
Read More
Advanced equipment and technological process.
We have 5 bright annealed furnace with 30 mtrs in length, the highest temperature can reach 1350℃, and the tolerance between the set and real temperature could be within 2℃, and it ensures the mechanical properities and the quality of the pipe surface.
Straightening Machine, this equipment can ensure the straightness of our big OD pipes
More >>
Contact
Facebook/Cindy twitter/Cindy linkedin/Cindy skype/cindydu82
E-Mail:
mt@mtstainlesssteel.com
Tel:
+86-573-82626532
+86-573-82626531
+86-573-82717867
Fax:
+86-573-8271 8785
Download The Catalogue
Copyright © 2013 Jiaxing MT stainless steel co.,ltd. (MTSCO) All Rights Reserved. / Powered By Supplierlist.com